Laird Plastics - MAKROLON HYGARD® CG750

MAKROLON HYGARD® CG750

MAKROLONHYGARD® CG750 laminate is a three-ply MAKROLON polycarbonate sheet for higher level architectural glazing security applications.

MAKROLON HYGARD CG750 laminate features abrasion and UV resistant surfaces for extended service life in harsh environments.

Applications:

MAKROLONHYGARD CG750 laminate is used in jails, detention facilities, and psychiatric hospitals as containment glazing for protection against forced entry/egress into or from controlled areas.

Typical Physical Properties

Gauge/Tolerance

.780 ±5%

Weight

4.9 lbs./s.f.

Shading Coefficient

.87

% Light Transmittance

77% (clear)

Colors

Standard:Clear
Custom Colors on request

Sheet Sizes

Standard:	38˝ x 96˝ 48˝ x 96˝ 60˝ x 96˝
Custom Sizes on request

Sheffield Plastics Inc. will not be responsible for the use of this information relative to actual application. Users must make their own determination of its suitability for their specific application. No warranty is made for the fitness of any product, and nothing herein waives any of the seller’s conditions of sale.

GLAZING INFORMATION

Use of structural security framing systems with equal or greater forced entry and/or ballistics ratings as the selected MAKROLON HYGARD laminate is recommended.
Size MAKROLON HYGARD laminates to allow for a minimum of 1˝ edge engagementin the frame, with sufficient rabbet depth for material expansion (approx. 1/16˝/ft.).
Use wet or dry sealants/gaskets that are compatible with polycarbonate.
Remove protective masking after glazing operations are completed and before prolonged exposure to direct sunlight, moisture, or high temperature.

CLEANING INSTRUCTIONS

Rinse with clean water to remove abrasive dust and dirt.
Wash with soap or mild detergent using a sponge or soft cloth. Do not scrub.
Rinse once more. Dry with a soft cloth or chamois to prevent water spots.
To remove labels, stickers, or grease, rub gently with a cloth wetted thoroughly in VM&P naptha or isopropyl alcohol. Wash and rinse. Do not use razor blades, scrapers, or squeegees.

FORCED ENTRY, BALLISTICS RATINGS

H.P. WHITE TP 0500.01 Level IV Step 31
H.P. WHITE TP 0500.01 Level B Ballistics (9mm)
ASTMF 1233 Class IV Step 26/p>

Product Specification

MAKROLON HYGARD CG750 laminate:
Three-ply, clear MAKROLON polycarbonate sheet constructed as follows:

1/8˝ MAKROLON polycarbonate sheet with high AR abrasion-resistant surface
Polyurethane bonding interlayer
1/2˝ MAKROLON polycarbonate sheet
Polyurethane bonding interlayer
1/8˝ MAKROLON polycarbonate sheet with high AR abrasion-resistant surface

Material shall have a flexural strength of at least 13,500 psi per ASTM D-790; and shall have AR (high performance abrasion-resistant) surfaces for enhanced service life and resistance to marring. Material shall exhibit a self ignition temperature of 1077°F and a flash ignition temperature of 872°F (ASTM D-1929), and conform with ICBO & BOCA Model Building Codes as a CC-1 rated Approved Light Transmitting Plastic.